ALPININA
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 8,2 MPa
Volumetric Weight 2696 Kg/m3
Water Absorption 0.2 %
Aparent Porosity 0.5 %
Thermal Lin. Expan. Coef. 4.3x10^-6 per º C
Abrasion Test 1.9 mm
Impact Test 45 cm
![vidraco-ataija-mix.jpg](https://static.wixstatic.com/media/dc1acb_2adf043c202f4dda83a90d739e68953a~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/vidraco-ataija-mix.jpg)
VIDRAço ATAíja Mix
MICROSCOPIC PROPERTIES
​
Calcite 99%
Quartzo 1%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 198 Kg/cm2
Compression BL after FT 1653 Kg/cm2
Compression Break. Load 1785 Kg/cm2
Volumetric Weight 2670 Kg/m3
Water Absorption 0.4 %
Aparent Porosity 0.93 %
Thermal Lin. Expan. Coef. 3.6 10^6perºC
Abrasion Test 2.9 mm
Impact Test 35/40 cm
![vidraco-ataija-azul.jpg](https://static.wixstatic.com/media/dc1acb_cfff9d09bcb2431fac814c85d1f78345~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/vidraco-ataija-azul.jpg)
VIDRAÇO ATAÍJA AZUL
MICROSCOPIC PROPERTIES
​
Calcite 99%
Quartzo 1%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 198 Kg/cm2
Compression BL after FT 653 Kg/cm2
Compression Break. Load 1785 Kg/cm2
Volumetric Weight 2670 Kg/m3
Water Absorption 0.4 %
Aparent Porosity 0.93 %
Thermal Lin. Expan. Coef. 3.6 10^6perºC
Abrasion Test 2.9 mm
Impact Test 35/40 cm
![moca-creme.jpg](https://static.wixstatic.com/media/dc1acb_99021ad9af0b480c91160d8886ed1c27~mv2.jpg/v1/crop/x_0,y_0,w_877,h_800/fill/w_90,h_82,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/moca-creme.jpg)
LIMESTONE REAL
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Thermal Lin. Expan. Coef. 3.1 10^6perºC
Abrasion Test 3.5 mm
Impact Test 35/40 cm
Bending Strength 144 Kg/cm2
Compression BL after FT 930 Kg/cm2
Compression Break. Load 917 Kg/cm2
Volumetric Weight 2478 Kg/m3
Water Absorption 2.9 %
Aparent Porosity 7.6 %
![MVC_Limestone Jurassic.jpg](https://static.wixstatic.com/media/dc1acb_ec07f5505edf4f9aa0744aa4c191c6cd~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/MVC_Limestone%20Jurassic.jpg)
Limestone jurassic
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 144 Kg/cm2
Compression BL after FT 930 Kg/cm2
Compression Break. Load 917 Kg/cm2
Volumetric Weight 2478 Kg/m3
Water Absorption 2.9 %
Aparent Porosity 7.6 %
Thermal Lin. Expan. Coef. 3.1 10^6perºC
Abrasion Test 3.5 mm
Impact Test 35/40 cm
![codacal-real-amaciado.jpg](https://static.wixstatic.com/media/dc1acb_0d6f3fad05fb4a4daecbb09eeb2ed3f3~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/codacal-real-amaciado.jpg)
Codaçal real
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 108 Kg/cm2
Compression BL after FT 555 Kg/cm2
Compression Break. Load 550 Kg/cm2
Volumetric Weight 2346 Kg/m3
Water Absorption 5.12 %
Aparent Porosity 12.03 %
Thermal Lin. Expan. Coef. 5.7 10^6perºC
Abrasion Test 5.9 mm
Impact Test 35 cm
![codacal-dunas.jpg](https://static.wixstatic.com/media/dc1acb_9f1b53fb8e7f4f9186a7d1958d1a5f4f~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/codacal-dunas.jpg)
CODAÇAL DUNAS
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Thermal Lin. Expan. Coef. 5.7 10^6perºC
Abrasion Test 5.9 mm
Impact Test 35 cm
Bending Strength 108 Kg/cm2
Compression BL after FT 555 Kg/cm2
Compression Break. Load 550 Kg/cm2
Volumetric Weight 2346 Kg/m3
Water Absorption 5.12 %
Aparent Porosity 12.03 %
![creme-mos.jpg](https://static.wixstatic.com/media/dc1acb_8355dd404f0d48a4861625388d0a103c~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/creme-mos.jpg)
Creme mós
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 108 Kg/cm2
Compression BL after FT 555 Kg/cm2
Compression Break. Load 550 Kg/cm2
Volumetric Weight 2346 Kg/m3
Water Absorption 5.12 %
Aparent Porosity 12.03 %
Thermal Lin. Expan. Coef. 5.7 10^6perºC
Abrasion Test 5.9 mm
Impact Test 35 cm
![moca-creme.jpg](https://static.wixstatic.com/media/dc1acb_99021ad9af0b480c91160d8886ed1c27~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/moca-creme.jpg)
moca creme
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Impact Test 40 cm
Bending Strength 196 Kg/cm2
Compression BL after FT 867 Kg/cm2
Compression Break. Load 927 Kg/cm2
Volumetric Weight 2515 Kg/m3
Water Absorption 2.34 %
Aparent Porosity 5.9 %
Thermal Lin. Expan. Coef. 5.3 10^6perºC
Abrasion Test 4 mm
![figueiras-beje-f4-f5.jpg](https://static.wixstatic.com/media/dc1acb_980a1812290242c69ee80c338eeadc8d~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/figueiras-beje-f4-f5.jpg)
FIGUEIRAS BEJE F4/F5
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 293 Kg/cm2
Compression Break. Load 1562 Kg/cm2
Volumetric Weight 2650 Kg/m3
Water Absorption 0.07 %
Aparent Porosity 1.65 %
Thermal Lin. Expan. Coef. 6.2 %
Abrasion Test 1.9 mm
![figueiras-blue-f4-f5.jpg](https://static.wixstatic.com/media/dc1acb_a39b2c70b6924ab8b85c645e1b8b849a~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/figueiras-blue-f4-f5.jpg)
FIGUEIRAS BLUE F4/F5
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 293 Kg/cm2
Compression Break. Load 1562 Kg/cm2
Volumetric Weight 2650 Kg/m3
Water Absorption 0.07 %
Aparent Porosity 1.65 %
Thermal Lin. Expan. Coef. 6.2 %
Abrasion Test 1.9 mm
![figueiras-mix.jpg](https://static.wixstatic.com/media/dc1acb_5025c5f905b9494e959e26c898c32731~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/figueiras-mix.jpg)
FIGUEIRAS MIX
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 293 Kg/cm2
Compression Break. Load 1562 Kg/cm2
Volumetric Weight 2650 Kg/m3
Water Absorption 0.07 %
Aparent Porosity 1.65 %
Thermal Lin. Expan. Coef. 6.2 %
Abrasion Test 1.9 mm
![gascogme-beje.jpg](https://static.wixstatic.com/media/dc1acb_43cf2882176f4499a323c5a308fb83e7~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/gascogme-beje.jpg)
GASCOGNE BEJE
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 105 Kg/cm2
Compression BL after FT 1030 Kg/cm2
Compression Break. Load 953 Kg/cm2
Volumetric Weight 2567 Kg/m3
Water Absorption 1.73 %
Aparent Porosity 4.44 %
Thermal Lin. Expan. Coef. 5 10^6perºC
Abrasion Test 4.2 mm
Impact Test 40 cm
![rosal.jpg](https://static.wixstatic.com/media/dc1acb_2c590433ecf84698b50edcc9b2197835~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/rosal.jpg)
ROSAL
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 123 Kg/cm2
Compression BL after FT 457 Kg/cm2
Compression Break. Load 493 Kg/cm2
Volumetric Weight 2305 Kg/m3
Water Absorption 5.47 %
Aparent Porosity 12.61 %
Thermal Lin. Expan. Coef. 3.3 10^6perºC
Abrasion Test 9.3 mm
Impact Test 25 cm
![vidraco-moleanos.jpg](https://static.wixstatic.com/media/dc1acb_152da6133ad34507b8d9759edf680106~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/vidraco-moleanos.jpg)
Vidraço moleanos
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Thermal Lin. Expan. Coef. 5 10^6perºC
Abrasion Test 4.2 mm
Impact Test 40 cm
Bending Strength 105 Kg/cm2
Compression BL after FT 1030 Kg/cm2
Compression Break. Load 953 Kg/cm2
Volumetric Weight 2567 Kg/m3
Water Absorption 1.73 %
Aparent Porosity 4.44 %
![atlantic-blue_1.jpg](https://static.wixstatic.com/media/dc1acb_a3f9f384fd2c4d4ea908286467e5ba0a~mv2.jpg/v1/fill/w_67,h_100,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/atlantic-blue_1.jpg)
Atlantic blue
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 198 Kg/cm2
Compression BL after FT 1885 Kg/cm2
Compression Break. Load 2100 Kg/cm2
Volumetric Weight 2650 Kg/m3
Water Absorption 0.5 %
Aparent Porosity 0.95 %
Abrasion Test 0.9 mm
![rosal rafael.jpg](https://static.wixstatic.com/media/dc1acb_6282140547a145deb83c3bd6e9929f00~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/rosal%20rafael.jpg)
Rosal Rafael
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 108 Kg/cm2
Compression BL after FT 555 Kg/cm2
Compression Break. Load 550 Kg/cm2
Volumetric Weight 2346 Kg/m3
Water Absorption 5.12 %
Aparent Porosity 12.03 %
Thermal Lin. Expan. Coef. 5.7 10^6perºC
Abrasion Test 5.9 mm
Impact Test 35 cm
![moleanos white.jpg](https://static.wixstatic.com/media/dc1acb_17419ab442244ed6915080740d885aca~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/moleanos%20white.jpg)
MOLEANOS WHITE
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 144 Kg/cm2
Compression BL after FT 930 Kg/cm2
Compression Break. Load 917 Kg/cm2
Volumetric Weight 2478 Kg/m3
Water Absorption 2.9 %
Aparent Porosity 7.6 %
Thermal Lin. Expan. Coef. 3.1 10^6perºC
Abrasion Test 3.5 mm
Impact Test 35/40 cm
![lioz-dourado-polido.jpg](https://static.wixstatic.com/media/dc1acb_36b4d4253c2f4cd3b461f0b1460d6e7f~mv2.jpg/v1/fill/w_90,h_56,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/lioz-dourado-polido.jpg)
LIOZ DOURADO
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Bending Strength 209 Kg/cm2
Compression BL after FT 1380 Kg/cm2
Compression Break. Load 1050 Kg/cm2
Volumetric Weight 2703 Kg/m3
Water Absorption 0.11 %
Aparent Porosity 0.31 %
Thermal Lin. Expan. Coef. 3.3 10^6perºC
Abrasion Test 2.2 mm
Impact Test 45 cm
![lioz-abancado-polido.jpg](https://static.wixstatic.com/media/dc1acb_9a9715a55e3b4e1bb2e7abdcd44e5348~mv2.jpg/v1/fill/w_90,h_60,al_c,q_80,usm_0.66_1.00_0.01,blur_2,enc_auto/lioz-abancado-polido.jpg)
LIOZ ABAnCADO
MICROSCOPIC PROPERTIES
​
Calcite 100%
PHISICAL-MECHANICAL PROPERTIES
​
Water Absorption 0.11 %
Aparent Porosity 0.31 %
Thermal Lin. Expan. Coef. 3.3 10^6perºC
Abrasion Test 2.2 mm
Impact Test 45 cm
Bending Strength 209 Kg/cm2
Compression BL after FT 1380 Kg/cm2
Compression Break. Load 1050 Kg/cm2
Volumetric Weight 2703 Kg/m3